Control of self‐organized low‐dimensional morphology in poly(styrene‐b‐4vinylpyridine)/polystyrene blend thin films

The surface morphologies of poly(styrene‐b‐4vinylpyridine) (PS‐b‐P4VP) diblock copolymer and homopolystyrene (hPS) binary blend thin films were investigated by atomic force microscopy as a function of total volume fraction of PS (?_PS) in the mixture. It was found that when hPS was added into symmetric PS‐b‐P4VP diblock copolymers, the surface morphology of this diblock copolymer was changed to a certain degree. With ?_PS increasing at first, hPS was solubilized into the corresponding domains of block copolymer and formed cylinders. Moreover, the more solubilized the hPS, the more cylinders exist. However, when the limit was reached, excessive hPS tended to separate from the domains independently instead of solubilizing into the corresponding domains any longer, that is, a macrophase separation occurred. A model describing transitions of these morphologies with an increase in ?_PS is proposed. The effect of composition on the phase morphology of blend films when graphite is used as a substrate is also investigated. © 2004 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 3496–3504, 2004     

Influence of annealing and chain defects on the melting behaviour of poly(vinylidene fluoride)

The melting behaviour of poly(vinylidene fluoride) (PVDF) was investigated by differential scanning calorimetry (DSC) and small- and wide-angle X-ray scattering in order to study the influence of the chain defects content and of the temperature of annealing on the crystallization and melting behaviour.All the DSC scans show a double endotherm and the analysis of the data suggests that the low temperature endotherm is due to the melting of a population of thin lamellae, whose thickness increases during the annealing, but a high content of chain defects prevents the lamellar thickening and the main effect in this case is the crystallization of thin lamellae from a portion of polymer which did not crystallize during the quenching from the melt. Furthermore, the two melting endotherms, which are observed, can be partially ascribed to a melting-recrystallization process.Furthermore, stepwise isothermal cooling was performed in a differential scanning calorimeter followed by melting scans of fractionated PVDF samples to point out the possible presence of a series of endothermic peaks.     

RPS增容LDPE／PS研究

用ＨＡＡＫＥ、ＤＳＣ、ＩＲ等方法研究了侧基含有过氧键的反聚苯乙烯与ＬＤＰＥ之间的反应，并将其应用到ＬＤＰＥ／ＰＳ共混体系。考察了不同添加方式，交联助剂等对共混物力学性能、流变性能及微观结构的影响。     

Formation of β‐iPP in isotactic polypropylene/ethylene–propylene rubber blends: Effects of preparation method,composition, and thermal condition

The effects of preparation method, composition, and thermal condition on formation of β‐iPP in isotactic polypropylene/ethylene–propylene rubber (iPP/EPR) blends were studied using modulated differential scanning calorimeter (MDSC), wide angle X‐ray diffraction (WAXD), and phase contrast microscopy (PCM). It was found that the α‐iPP and β‐iPP can simultaneity form in the melt‐blended samples, whereas only α‐iPP exists in the solution‐blended samples. The results show that the formation of β‐iPP in the melt‐blended samples is related to the crystallization temperature and the β‐iPP generally diminishes and finally vanishes when the crystallization temperature moves far from 125 °C. The phenomena that the lower critical temperature of β‐iPP in iPP/EPR obviously increases to 114 °C and the upper critical temperature decreases to 134 °C indicate the narrowing of temperature interval, facilitating the formation of β‐iPP in iPP/EPR. Furthermore, it was found that the amount of β‐iPP in melt‐blended iPP/EPR samples is dependent on the composition and the maximum amount of β‐iPP formed when the composition of iPP/EPR blends is 85:15 in weight. The results through examining the effect of annealing for iPP/EPR samples at melt state indicate that this annealing may eliminate the susceptibility to β‐crystallization of iPP. However, only α‐iPP can be observed in solution‐blended samples subjected to annealing for different time. The PCM images demonstrate that an obvious phase‐separation happens in both melt‐blended and solution‐blended iPP/EPR samples, implying that compared with the disperse degree of EPR in iPP, the preparation method plays a dominant role in formation of β‐iPP. It is suggested that the origin of formation of β‐iPP results from the thermomechanical history of the EPR component in iPP/EPR. © 2007 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 45: 1704–1712, 2007     

多组分单体接枝聚丙烯/尼龙6反应共混物结晶行为研究

用多组分熔融接枝的方法将甲基丙烯酸缩水甘油酯 (GMA)和苯乙烯 (St)共同接枝到聚丙烯 (PP)上 ,制得具有较高GMA接枝率的多单体接枝聚丙烯 ,PP g (GMA co St) .将PP g (GMA co St)与尼龙 6 (PA6 )进行共混 ,利用扫描电镜 (SEM) ,差示扫描量热计 (DSC)和广角X射线衍射 (WAXD)对共混物的形态和结晶进行了研究 .在共混过程中 ,PP g (GMA co St)与PA6反应原位生成了PP g PA6 ,有效改善了共混物的相容性 ,分散相尺寸明显减小 .在PP g (GMA co St) PA6为 3 7的体系中 ,PP g (GMA co St)出现分级结晶现象 ,其在较低温度下的结晶属于均相成核结晶 .在PP g (GMA co St) PA6为 7 3的体系中 ,由于PA6相分散细微 ,在通常结晶温度下不结晶 ,而是在低温下均相成核与PP g (GMA co St)同时结晶 .WAXD证实体系中接枝PP ,PA6为分别结晶 ,无共晶或新的晶型产生     

接枝共聚物氯化聚乙烯—苯乙烯对聚苯乙烯的共混改性

用氯化聚乙烯接枝苯乙烯共聚物（ＣＰＥ－ｇ－Ｓｔ）和氯化聚乙烯（ＣＰＥ）对聚苯乙烯（ＰＳ）进行共混改性。当ＣＰＥ含量为２５％时，用ＣＰＥ－ｇＳｔ改性的共混物的冲击强度为１８．５ｋＪ．ｍ＾－＾２，是用ＣＰＥ改性的共混物冲击强度的２．１倍；其拉伸强度不低于３４ＭＰａ。     

γ-射线辐照对尼龙6纤维结构的影响

<正> 过去的大多数研究表明,高能射线辐照会引起聚乙烯及聚丙烯等稀烃类聚合物分子链交联及降解,而且会导致结晶度下降。张利华等人最近的研究表明,对于尼龙1010塑料,仅当辐照剂量高到一定程度后,辐照才会破坏结晶。此外,Stowe等人曾经研究过近紫外线对尼龙66纤维结构的影响,结果表明,在空气气氛中的近紫外辐照主要导致尼龙66纤维降解,并使纤维结晶度提高。有关高能射线辐照对高度取向的合成纤维结构及性能的影响的研究尚不多见。本工作将讨论γ-射线对于尼龙6纤维结构的影响。     

含间苯基聚芳醚酮的合成与性能研究

含间苯基聚芳醚酮的合成与性能研究林权，张万金，吴忠文，尹玖梅（吉林大学化学系，长春，１３００２１）（中国科学院长春应用化学研究所）关键词聚芳醚酮，间苯基，熔点，结晶度聚芳醚酮作为一类耐高温特种工程塑料，由于具有优异的热、电、机械性能，已被广泛应用于电...     

弹性体共混改性聚丙烯的增韧机理

阐述了以聚丙烯（ＰＰ）／高密度聚乙烯（ＨＤＰＥ）为复合基体，苯乙烯－丁二烯－苯乙烯（ＳＢＳ）为增韧剂经三元共混所得的性能优异的一类新材料．从三个层次（形貌结构转变、宏观力学响应和裂尖过程区演化）系统地探讨了其增韧机理．结果表明由形貌结构控制和对早期体膨胀变形抑制可造成裂尖平面应变区的超钝化从而达到增韧．     

咪唑类离子液体结构与熔点的构效关系及其基本规律

熔点是界定、研究离子液体及其使用过程的一个重要参考指标,因此研究离子液体分子结构与熔点之间的构效关系及其基本规律有特别重要的意义。本文以从近两百遍文献及Beilstein Gmelin网络数据库中收集的约900种咪唑类离子液体中的384种咪唑类离子液体的熔点数据为依据,考察了离子液体分子结构与熔点之间的构效关系及其基本规律,这对离子液体的设计合成及应用有指导作用。